LUBENZ ULTIMATE HIGH TEMPERATURE CLAY BASED GREASE are high temperature greases, formulated with
bentonite clay based thickener and extreme pressure additive system to provide extra protection against wear,
rusting and water washout especially in industrial equipment operating under heavy loads and high
temperatures. They are available in NLGI grades ranging from 00 to 3 with base oil viscosity of ISO VG 150 &
320. It retains its consistency at high temperatures and provides good storage stability.
![high temperature grease](https://lubenzlubricants.com/wp-content/uploads/2023/03/ultimate-high-271x300.jpeg)
high temperature grease
Features & Benefits
● Outstanding Non-melting capability – protects bearing at very high operating temperatures where
conventional soap-based greases fail to provide satisfactory lubrication.
● Good extreme pressure & anti-wear properties – protects bearing surfaces against severe wear, even
under high load conditions.
● Excellent Oxidation and Thermal stability – protects against deposit formation at very high operating
temperatures, thus maintains the life and performance of grease.
● Excellent resistance to water washout – resists washout of grease in equipment and provides good
lubrication even in presence of water.
● Excellent retention of consistency – resists grease softening in application, where very high temperatures
and mechanical working leads to subsequent loss of lubrication performance and leakage.
Applications
Application
LUBENZ ULTIMATE HIGH TEMPERATURE CLAY BASED GREASE are suitable for below applications:
● Drying Ovens
● Jaw Crushers
● Kiln cars
● Steel Mills
● Hot Rolling Mills
● Aluminum, Cement, Glass and Rubber plants
Characteristics
LUBENZ ULTIMATE HIGH TEMPERATURE CLAY BASED GREASE |
Test Method |
Units |
HT-EP00 |
HT-EP0 |
HT-EP1 |
HT-EP2 |
HT-EP3 |
NLGI Grade |
ASTM D 217 |
— |
00 |
0 |
1 |
2 |
3 |
Thickener Type |
— |
— |
Bentonite Clay |
Bentonite Clay |
Bentonite Clay |
Bentonite Clay |
Bentonite Clay |
Penetration,
Worked @ 25 0C |
ASTM D 217 |
0.1mm |
400-430 |
355-385 |
310-340 |
265-295 |
220-250 |
Viscosity @ 40 0C |
ASTM D 445 |
cSt |
320 |
160 |
160 |
160 |
160 |
Dropping Point |
ASTM D 566 |
°C |
– |
>300 |
>300 |
>300 |
>300 |
4-Ball Wear, Scar |
ASTM D 2266 |
mm |
0.5 |
0.4 |
0.4 |
0.4 |
0.4 |
4-Ball Weld Load |
ASTM D 2596 |
Kg |
240 |
250 |
250 |
250 |
250 |
The above figures are typical of blends with normal production tolerance and do not constitute a specification.